High Magnetic Permeability Dt4c Dt4e Steel Bar High Purity Iron Rod for Magnet Production

Product Description

Raw material	Tool steel d2 k110 skd11 Bar
Material	Hot work die steel: H13, 8407, 8418, FDAC, 4Cr5MoVSi, 1.2343, 1.2344, M302, M360, etc.  Cold work die steel: Cr12MoV, D2, Cr12, DF-2, XW-41, XW-42, DC53, SKD11 die steel, K110, K306, K360, 1.2379, etc.  Plastic mold steel: S136, 718H, CALMAX, S136H, NAK101, NAK80, NAK-PRM, 1.2711, 1.231, 1.2083, M200, M340, M238, P20, P20+Ni, MLQ, etc.
Size	Width: 1000mm,1219mm,1250mm,1500mm,1800mm,2000mm,2200mm,2500mm Length: 2000mm,2438mm,3000mm,6000mm Thickness: 0.35mm-200mm
Application	Used as reinforcement, bolts and various mechanical parts or as seamless steel tube blanks
Surface	Black Surface, Milled surface
Packaging	Waterproof paper,and steel strip packed,Standard Export seaworthy package suit for all kinds of transport or as required.

Die steel is used to make cold die, hot forging die, die casting die and other steel types. Moulds are the main processing tools for manufacturing parts in machinery manufacturing, radio instruments, motors, electrical appliances and other industrial sectors. The quality of the mold directly affects the quality of the pressure processing process, the accuracy of the product, and the production cost. The quality and service life of the mold are mainly affected by the mold material and heat treatment in addition to the reasonable structure design and processing accuracy.
 

2: AISI H13 Steel equivalent

Country	China	Japan	Germany	USA	UK
Standard	GB/T 1299	JIS G4404	DIN EN ISO4957	ASTM A681	BS 4659
Grade	4Cr5MoSiV1	SKD61	1.2344/X40CrMoV5-1	H13

3: AISI H13 steel chemical composition

Grade	C		Mn		P	S	Si		Cr		V		Mo
H13	0.32	0.45	0.2	0.6	0.03	0.03	0.8	1.25	4.75	5.5	0.8	1.2	1.1	1.75
1.2344 / X40CrMoV5-1	0.35	0.42	0.25	0.5	0.03	0.02	0.8	1.2	4.8	5.5	0.85	1.15	1.1	1.5
SKD61	0.35	0.42	0.25	0.5	0.03	0.02	0.8	1.2	4.8	5.5	0.8	1.15	1.0	1.5

Heat Treatment
Annealing
    Heat slowly to 1550°-1650°F, hold until entire mass is heated through, and cool slowly in the furnace (40F per hour) to about 1000°F, after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
Stress Relieving
    When desirable to relieve the strains of machining, heat slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving). Â
Preheat Prior to Hardening
    Warm slightly before charging into the preheat furnace, which should be operating at 1400°-1500°F.
Hardening
    H13 tool steel is a steel having very high hardenability and should be hardened by cooling in still air. The use of a salt bath or controlled atmosphere furnace is desirable to minimize decarburization, and if not available, pack hardening in spent pitch coke is suggested. The temperature employed is usually 1800°-1850°F, depending on size section.
Quenching
    Quench in still air or dry air blast. If complicated forms are to be hardened, an interrupted oil quench can be used. Quench part in oil and remove from bath when it just loses its color (1000°-1100°F). Finish cooling to below 150°-125°F in air, then temper immediately.
Tempering
    Tempering practice may vary with size and application, but is usually performed in the range of maximum secondary hardness or higher. Double tempering is recommended. The results below is H13 that was air quenched from 1800°F and tempered for 4 hours at various temperatures. The results may be used as a guide, keeping in mind that parts of heavy section or mass may be several points lower in hardness.

 

7: Delivery condition
    For hot forged or hot rolled bar, usually the delivery condition is hot forged or rolled, annealed, rough turned.
    For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface.

    For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.

FAQ

Q1:What product information must I provide before making a purchase?
Please provide the grade, width, thickness, and surface treatment requirements, as well as the quantities you require.

Q2:What shipping ports are there?
We normally ship from Shanghai, Tianjin, Qingdao, and Ningbo ports

Q3:What are your payment terms?
30% T/T in advance and 70% balance before shipment or based on BL copy or LC at sight.

Q4:What about product pricing information?
Prices vary due to changes in raw material prices on a regular basis.

Q5:Is it possible to send samples?
Of course, we offer free samples and express shipping to customers all over the world.

Q6:Do you offer a service for customized products?
Yes, we can produce according to your specifications and drawings.

Q7:Can you assist me in importing steel products for the first time?
Yes, we have shipping agent who will arrange the shipment with you.

Q8. What is your delivery time?
Within 7 working days after receiving your balance payment.