| Customization: | Available |
|---|---|
| Type: | Alloy Steel Bar |
| Standard: | AISI, ASTM, DIN, JIS, GB |
|
Still deciding? Get samples of US$ 50/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
|
Raw material
|
Tool steel d2 k110 skd11 Bar
|
|
|
Hot work die steel: H13, 8407, 8418, FDAC, 4Cr5MoVSi, 1.2343, 1.2344, M302, M360, etc.
Cold work die steel: Cr12MoV, D2, Cr12, DF-2, XW-41, XW-42, DC53, SKD11 die steel, K110, K306, K360, 1.2379, etc.
Plastic mold steel: S136, 718H, CALMAX, S136H, NAK101, NAK80, NAK-PRM, 1.2711, 1.231, 1.2083, M200, M340, M238, P20, P20+Ni, MLQ, etc.
|
|
|
Width: 1000mm,1219mm,1250mm,1500mm,1800mm,2000mm,2200mm,2500mm Length: 2000mm,2438mm,3000mm,6000mm Thickness: 0.35mm-200mm |
|
Application
|
Used as reinforcement, bolts and various mechanical parts or as seamless steel tube blanks
|
|
Surface
|
Black Surface, Milled surface
|
|
Packaging
|
Waterproof paper,and steel strip packed,Standard Export seaworthy package suit for all kinds of transport or as required.
|
2: AISI H13 Steel equivalent
| Country | China | Japan | Germany | USA | UK |
| Standard | GB/T 1299 | JIS G4404 | DIN EN ISO4957 | ASTM A681 | BS 4659 |
| Grade | 4Cr5MoSiV1 | SKD61 | 1.2344/X40CrMoV5-1 | H13 |
3: AISI H13 steel chemical composition
| Grade | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| H13 | 0.32 | 0.45 | 0.2 | 0.6 | 0.03 | 0.03 | 0.8 | 1.25 | 4.75 | 5.5 | 0.8 | 1.2 | 1.1 | 1.75 |
| 1.2344 / X40CrMoV5-1 |
0.35 | 0.42 | 0.25 | 0.5 | 0.03 | 0.02 | 0.8 | 1.2 | 4.8 | 5.5 | 0.85 | 1.15 | 1.1 | 1.5 |
| SKD61 | 0.35 | 0.42 | 0.25 | 0.5 | 0.03 | 0.02 | 0.8 | 1.2 | 4.8 | 5.5 | 0.8 | 1.15 | 1.0 | 1.5 |
Heat Treatment
Annealing
Heat slowly to 1550°-1650°F, hold until entire mass is heated through, and cool slowly in the furnace (40F per hour) to about 1000°F, after which cooling rate may be increased. Suitable precautions must be taken to prevent excessive carburization or decarburization.
Stress Relieving
When desirable to relieve the strains of machining, heat slowly to 1050°-1250°F, allow to equalize, and then cool in still air (Strain Relieving). Â
Preheat Prior to Hardening
Warm slightly before charging into the preheat furnace, which should be operating at 1400°-1500°F.
Hardening
H13 tool steel is a steel having very high hardenability and should be hardened by cooling in still air. The use of a salt bath or controlled atmosphere furnace is desirable to minimize decarburization, and if not available, pack hardening in spent pitch coke is suggested. The temperature employed is usually 1800°-1850°F, depending on size section.
Quenching
Quench in still air or dry air blast. If complicated forms are to be hardened, an interrupted oil quench can be used. Quench part in oil and remove from bath when it just loses its color (1000°-1100°F). Finish cooling to below 150°-125°F in air, then temper immediately.
Tempering
Tempering practice may vary with size and application, but is usually performed in the range of maximum secondary hardness or higher. Double tempering is recommended. The results below is H13 that was air quenched from 1800°F and tempered for 4 hours at various temperatures. The results may be used as a guide, keeping in mind that parts of heavy section or mass may be several points lower in hardness.
7: Delivery condition
For hot forged or hot rolled bar, usually the delivery condition is hot forged or rolled, annealed, rough turned.
For hot forged plate, usually the delivery condition is hot forged, annealed, milled surface.
For hot rolled plate, usually the delivery condition is hot rolled, annealed, black surface.